Mössbauer studies of a martensitic transformation and of cryogenic treatments of a D2 tool steel
Authors: B.F.O. Costa, M. Blumers, A. Kortmann, W. Theisen, A.C. Batista , G. Klingelhöfer
Ref.: Hyperfine Interactions 219, 135-139 (2013)
Abstract: A D2 tool steel X153CrVMo12 with composition C1.53 Cr12 V0.95 Mo0.80 Mn0.40(wt% Fe balanced) was studied by use of Mossbauer spectroscopy and X-ray diffraction. It was observed that the study of carbides by X-ray diffraction was difficult while Mossbauer spectroscopy gives some light on the process occurring during cryogenic treatment. With the increase of the martensitic phase the carbides decrease and are dissolved in solid solution of martensite as well as the chromium element.